Mgbagwoju ihe mejupụtara seramiiki nwere eriri bụ ụdị pụrụ iche nke nwere akwa akwa nke ihe seramiiki na-ekpuchi n'ime ya.

Zitere anyị email

Nkọwa ngwaahịa

Mkpado ngwaahịa

Akụkụ ceramik nwere akara na agbagọ

A Mgbakọ ngwakọta mejupụtara seramiikibụ ụdị agbagọ pụrụ iche nke nwere akwa akwa seramiiki na-ekpuchi ime ya.Nke a na-ehulata imewe nwere ike n'ụzọ zuru ezu leverage uru nke ma ọla na ceramik, n'ịhụ ike na machinability nke ọla na elu okpomọkụ, eyi na-eguzogide, na corrosion-eguzogide Njirimara nke ceramik.

Ike & Kọmpat ;Dị nro & Inert;Na-eguzogide elu-abrasion & corrosion seramiiki wear lining

N'ime ụlọ ọrụ ọ bụla nke usoro a, karịsịa ígwè na ciment, corrosion na abrasion na-eduga n'oge dị ukwuu nke osisi ahụ.Ọzọkwa, ndụ bara uru nke akụrụngwa n'onwe ya nwere ike ịdaba n'ihi oke abrasive nke ihe ndị a na-eji.Ya mere, 'wear method' na-ebute nkwụsị, nnọchi, wdg, nke dị oke ọnụ, na-ebute mfu na ụda nde rupees.Maka iguzogide iyi, eriri seramiiki, ọkpọkọ kwụ ọtọ, wdg, dị mma.

Dabere na ọtụtụ afọ nke omume, Kingcera webatara teknụzụ dị elu site na mba ofesi, gbanwee usoro ndozi seramiiki site na tapawa ọdịnala ọdịnala gaa na njikọta nke inorganic nrapado na-ekpo ọkụ na-ekpo ọkụ, ịgbado ọkụ na ịgbado ọkụ ugboro atọ, wee mụbaa okpomọkụ ojiji ruo 750 ℃.Kpochapụ nsogbu nke seramiiki na-adapụ na okpomọkụ dị elu, na-eme ka ntụkwasị obi dịkwuo elu, na-agbatịkwu ndụ nke ngwa ahụ ugboro 10-20.

Atụmatụ

Nnukwu iguzogide ụdị kemịkalụ niile

Nnukwu iguzogide abrasion na-amị amị

Ikike mmiri na-adịghị mma na elu dị larịị na-ebute ngwa ngwa ngwa ngwa

Nwere ike iguzogide okpomọkụ ruo 200 Celsius

Enwere ike ịmepụta NJ pere mpe nke 100 mm

Nkọwa nka nka

• A na-eji seramiiki lined bends na-ebufe ihe nwere nnukwu ọsọ.

• A na-eji ihe mkpuchi seramiiki maka ngwa radius dị mkpụmkpụ Bend.

• ọkpụrụkpụ tile dị site na 6 mm ruo 50 mm.

• Nha tube (cylinder) sitere na NJ 40 ruo 150 mm.

• Ụdị Taịlị: Plain / Tapered, Pastable / Weldeable, Pressed/Cast.

Nkọwapụta akụrụngwa

Otu	HC92	HC95	HCT95	HC99	HC-ZTA
Al₂O₃	≥92%	≥95%	≥ 95%	≥ 99%	≥75%
ZrO2	/	/	/	/	≥21%
Njupụta (g/cm³)	3.60	3.65g	3.70	3.83	4.10
HV 20	≥950	≥1000	≥1100	≥1200	≥1350
Nkume Hardness HRA	≥82	≥85	≥88	≥90	≥90
Ehulata Ike MPa	≥220	≥250	≥300	≥330	≥400
Ike mkpakọ MPa	≥1050	≥1300	≥1600	≥1800	≥2000
Ike mgbajiji (KIc MPam 1/2)	≥3.7	≥3.8	≥4.0	≥4.2	≥4.5
Yiri olu (cm³⁾	≤0.25	≤0.20	≤0.15	≤0.10	≤0.05